Standard:
CHINA |
GB/T 3077-2015 GB/T 34484.2-2018 GB/T 17107-1997 JB/T 6396-2006 |
34Cr2Ni2Mo |
GERMANY |
DIN EN 10083-3:2007[TJC STEEL] DIN 17200:1987 |
34CrNiMo6 1.6582 |
Chemical Composition(%)
MATERIAL |
34Cr2Ni2Mo |
34CrNiMo6 |
C |
0.30~0.38 |
0.30~0.38 |
Si |
0.17~0.37 |
≤0.40 |
Mn |
0.50~0.80 |
0.50~0.80 |
P |
≤0.030[TJC STEEL] |
≤0.025 |
S |
≤0.030 |
≤0.035 |
Cr |
1.30~1.70 |
1.30~1.70 |
Ni |
1.30~1.70 |
1.30~1.70 |
Mo |
0.15~0.30 |
0.15~0.30 |
Mechanical Property(GB/T 3077-2015)
Sample Size(mm) |
Ø25 |
|
Heat Treatment(℃) |
Quenched(Oil Cooling) |
850 |
Tempered(Water,Oil Cooling) |
540 |
|
Mechanical Property |
TSMPa[TJC STEEL] |
≥1080 |
YSMPa |
≥930 |
|
A% |
≥10 |
|
Z% |
≥50 |
|
AKU2/J |
≥71 |
|
HardnessHBW |
Annealed or Tempered in High Temperature |
≤269 |
Performance Purpose:
34CrNiMo6 is similar to 42CrMo in performance and has high strength and good toughness. It is used to manufacture important structural [TJC STEEL]parts for high load work, such as wind turbine spindles, high-speed train axles, torsion shafts of armored vehicles, crankshafts and connecting rods for heavy diesel engines, and gears for other heavy duty parts.