A240/SUS 410S stainless steel plate is a low-carbon modification of 410 stainless steel, known for its excellent corrosion resistance, high strength, and heat resistance. It is widely used in various industries due to its favorable properties.

Physical Properties:

A240/SUS 410S stainless steel plate exhibits a density of approximately 7.7 g/cm³, providing good strength while maintaining a moderate weight. It has a melting point of around 1480-1530°C and a thermal conductivity of approximately 24.9 W/m·K.

Size Range:

Available in a wide range of sizes and thicknesses, A240/SUS 410S stainless steel plate typically ranges from 0.3 mm to 100 mm in thickness. Widths can extend up to 2000 mm, and lengths can reach up to 6000 mm, catering to diverse application requirements.

Chemical Composition:

The typical chemical composition of A240/SUS 410S stainless steel plate includes:

- Chromium (Cr): 11.5-13.5%

- Nickel (Ni): ≤0.60%

- Carbon (C): ≤0.08%

- Manganese (Mn): ≤1.0%

- Silicon (Si): ≤1.0%

- Phosphorus (P): ≤0.040%

- Sulfur (S): ≤0.030%

Mechanical Properties:

- Tensile Strength: ≥415 MPa

- Yield Strength: ≥205 MPa

- Elongation: ≥20%

These mechanical properties ensure reliable performance in various applications.

Hardness:

A240/SUS 410S stainless steel plate typically exhibits a Rockwell hardness of approximately B80.

Standard Compliance (ASTM A240, JIS G4304):

A240/SUS 410S stainless steel plate complies with international standards such as ASTM A240 and JIS G4304, ensuring quality and consistency in production.

Non-Destructive Testing Standard:

Standard non-destructive testing methods, including ultrasonic inspection, are employed to ensure the quality and integrity of A240/SUS 410S stainless steel plates.

Corrosion Resistance:

A240/SUS 410S stainless steel offers excellent corrosion resistance, particularly in mild atmospheric and mildly corrosive environments. It is resistant to oxidation and scaling at elevated temperatures.

Heat Treatment Condition:

A240/SUS 410S stainless steel plate is generally annealed at temperatures ranging from 760 to 815°C, followed by rapid cooling. This process helps improve its machinability and formability.

Main Applications:

- Automotive Industry: Used in exhaust systems, catalytic converters, and mufflers.

- Construction: Employed in architectural trim, building facades, and roofing.

- Kitchen Equipment: Utilized in sinks, countertops, and appliances.

- Petrochemical Industry: Found in refinery equipment, pipelines, and storage tanks.

- Industrial Furnaces: Used in furnace components and heat exchangers.

TJC Steel Supply Case:

TJC Steel (TJC Iron & Steel(Group) Co., Limited) is a leading supplier of A240/SUS 410S stainless steel plates, adhering strictly to international standards like ASTM A240 and JIS G4304. They provide high-quality stainless steel solutions for various industrial applications, ensuring customer satisfaction and reliability.